The box-type resistance furnace is not used correctly, it is really a "test of life"

Box-type resistance furnace can be used in laboratories, industrial and mining enterprises, scientific research units, etc. for element analysis and determination, and for heating small steel parts and other metals in heat treatment. The outer shell is welded with high-quality cold-rolled steel plate, and the furnace door adopts a side-opening structure, which is flexible to open and close. The internal insulation material is 0.4-0.6 lightweight insulation bricks and aluminum silicate fiber cotton to reduce heat storage and thermal conductivity. As a result, the studio has a large heat storage, a shorter heating time, the low temperature of the surface of the instrument rises, and the power loss and power consumption in the empty furnace are greatly reduced.
box-type resistance furnace adopts a closed working chamber, and the spiral shape uses an electric heating alloy wire as the heating element, and is wound on the wall of the working chamber. The furnace temperature during heating is the average temperature, which can prolong the service life. The high-temperature tubular resistance furnace studio uses high-temperature fire extinguishing pipes, using silicon carbide rods as heating elements, installed in the studio jacket, with high thermal efficiency. After unpacking, check whether the resistance furnace is in good condition and whether the accessories are complete. Place the resistance furnace on a dry platform or workbench indoors, and the controller should prevent vibration. The controller should not be placed near the resistance furnace to avoid overheating and the internal components cannot work properly. We will emphasize the correct use of any instrument. If the box-type resistance furnace is used incorrectly, it is really a "test of life".

Box type resistance furnace


1. Samples that cannot be directly placed in the furnace for disposal must be placed in a clean special crucible. The heat resistance of the crucible exceeds the temperature of the electric furnace. Do not use a box-type electric furnace with a high temperature to avoid burning the heating element. When the box-type electric furnace is heated, the furnace shell will also be heated. Keep the stove away from combustible materials and make it easy to dissipate heat.
2. Samples that cannot be placed directly in the furnace must be placed in a clean special crucible. The heat resistance of the crucible exceeds the temperature of the electric furnace. Do not use a box-type electric furnace with a high temperature to avoid burning the heating element. When the box-type electric furnace is heated, the furnace shell also generates heat. Keep the furnace away from flammable materials, and insist on easily dissipating heat outside the furnace.
3. However, the traditional box-type electric furnace technology is more advanced, and the maximum temperature of the furnace shell will not exceed 50 degrees. Even if you do not touch this temperature, it will not cause burns to the human body, but you must still pay attention to safety. The service life of the heating element depends on the oxide layer on its surface.
4. Destroying the oxidation layer will shorten the life of the heating element. Each shutdown will damage the oxide layer, so it should be used as long as possible after it is turned on, but the temperature for long-term use should be more than 50 degrees lower than the limit temperature of the electric furnace.
5. After repeated use of the box-type resistance furnace, the edge material of the furnace may crack. These cracks are caused by thermal shrinkage and have no effect on the quality of the furnace. When the box-type electric furnace is heated to more than 400 degrees, it cannot be heated too quickly, but it must be heated slowly, so as not to affect the service life of the furnace.